Stainless Steel 316 Pipe Fittings are made up of the 316 grade of stainless steel material. This is an austenitic stainless steel that is used most next to the 304 material. It has chromium nickel and molybdenum in its composition which makes it corrosion resistant than the 304 material. The SS 316 buttweld fittings are suitable for piping that is deployed in corrosive environments and in high strength applications. There are different kinds of SS 316 weld fittings that are used in different types of applications. The ASTM A403 WP 316 elbow is one of the most commonly used fittings which changes the direction of the pipeline.
The elbows could be of 45 degree angle or 90 degree angle normally. There are WP 316 reducer types such as the concentric and eccentric reducers both reducing the diameter of the pipe. There is also the a403 WP316 end cap which is used at the end of a pipe to terminate the flow. These caps could be permanently fitted with welding or be temporarily fitted with flanges and bolting. There are different standards in this grade such as the a403 grade WP316 fittings which are the pressure operation fittings. We supply the WP 316 tee, bend, elbow and all other types of fittings. Please contact Dinesh Industries for further details or information.
Table of Content
|Specifications||ASTM A403 / ASME SA403|
|Size||1/8” NB TO 48” NB.|
|Dimensions||ASME B16.28, ASME/ANSI B16.9, MSS-SP-43|
|Thickness||Sch 5s, Sch XXS, Sch 160s, Sch 10s, Sch 80s, Sch 40s|
|Type||Welded / Seamless / Fabricated|
|Form||Tee, Cross, Reducer, Elbow, Bend, Cap, Nipples Stub end|
Grade 316 stainless steel Fittings offer high creep strength, stress-to-rupture and tensile strength at high temperatures, as well as excellent corrosion resistance and strength properties, On A403 WP304 Fittings Annealing can be done between 1,900 – 2,100°F.
|SS 316||0.08 max||2.0 max||1.0 max||0.045 max||0.030 max||16.00 – 18.00||2.00 – 3.00||11.00 – 14.00||67.845 min|
|Density||Melting Point||Tensile Strength||Yield Strength (0.2%Offset)||Elongation|
|8.0 g/cm3||1400 °C (2550 °F)||Psi – 75000 , MPa – 515||Psi – 30000 , MPa – 205||35 %|
|SS 316||1.4401 / 1.4436||S31600||SUS 316||316S31 / 316S33||–||Z7CND17‐11‐02||X5CrNiMo17-12-2 / X3CrNiMo17-13-3|
|Mean Co-eff of Thermal Expansion (µm/m/°C)||Thermal Conductivity
|Specific Heat 0-100°C
|0-100°C||0-315°C||0-538°C||At 100°C||At 500°C|